Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity

Product Categories
Chongqing Leomed Technology Co., Ltd.
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Contact Now

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity

Brand Name : LEOTECH

Model Number : UT-ML

Certification : CE

Place of Origin : Chongqing, China

MOQ : 500 pcs

Price : 69.44

Payment Terms : T/T

Product Name : UT-ML Dental Zirconia Block

Product Specification : 98, 95, 92*75*30 mm

Thickness : 30 mm

Power Source : Manual

Warranty : 1 Year

After-sale Service : Online technical support

Quality Certification : FDA

Instrument classification : Class II

Color : 16 VITA Classical

Contact Now

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity
UT-ML Dental Zirconia Block
● High Strength ● High Transparency ● Natural

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity

UT-ML Multilayer Zirconia: Technical Profile

  • Composition: ≥99% purity, 8.0–10.0% Y2O3

  • Properties:

    • Translucency: 49–53% (1.0 mm)

    • Flexural Strength: 600–800 MPa

    • Hardness: 1150–1250 HV10

  • Safety: 0 cytotoxicity | <0.1 Bq/g radioactivity

  • Applications: Single crowns & 3-unit bridges

  • Sintering: 1500°C (1480–1510°C)


Product Parameters:
Model UT Multilayer 95mm
Size 95mm
Strength 600-800 MPa
Shades 16 VITA Classical.
Disc Sizes 9 thicknesses(10,12.14.16.18.20.22.25.30mm)



Technical Parameters:

1.Chemical composition

Components UT-ML
ZrO2+HfO2+Y2O3 ≥99%
Y2O3 8.0%-10.0%
Al2O3 ＜0.15%
Other Oxides ＜0.5%

2.Physical characteristics

Properties UT-ML
Density before sintering(g.cm-3) 3.15±0.05
Density after sintering(g.cm-3) 6.06±0.02
CTE(25-500℃)(K-1) (10.5±0.5)×10-6
Flexural strength after sintering(Mpa) 600-800
Translucency(1.0±0.02mm) 49%-53%
Fracture toughness(MPa.m1/2) 3.5-5.0
Hardness(HV10) 1150-1250
Accelerated aging surface monoclinic phase content ＜5%
Chemical solubility after sintering(μg.cm-2) ＜100
Cytotoxicity 0 Level
Radioactivity(Bq.g-1) ＜0.1
Sintering temperature(℃) 1480-1510
Recommend 1500

Indications For Use ≤3 units

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity



Sintering:

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity





Factory Display:
Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity


Application:
Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity
Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity
Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity


Exhibition:
Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity



Product Tags:

Low-Temp Sintered Zirconia Disc

      

1150-1250 HV10 Zirconia Disc

      
Quality Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 &lt;0.1 Bq/g Radioactivity wholesale

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Chongqing Leomed Technology Co., Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)
 
You May Like